cleavage pattern
英 [ˈkliːvɪdʒ ˈpætn]
美 [ˈkliːvɪdʒ ˈpætərn]
网络 分裂型式
双语例句
- Fractographic observations showed that hydrogen could induce surface cracks for smooth specimens and a cleavage fracture pattern for notch specimens at RT.
破断面观察结果显示，在室温中，氢气会导致平滑试片在表面形成裂纹，而在凹槽试片中产生劈裂破坏形态。 - Its explicitly explained how the cleavage step pattern is formed by the cleavage crack intersecting with screw dislocation.
本文对解理台阶的形成模型&解理裂纹与螺位错交割模型进行了诠释。 - Fracture surfaces show predominant cleavage river pattern with a small quantity of dimples in the core.
硅钢断口边缘呈现解理断裂的河流花样，心部存在少量的韧窝。 - The cleavage pattern of developing egg is holoblastic.
卵的分裂方式为全卵割型。 - The results showed that the HAZ impact toughness decreased with the increase in peak temperature and hence the fractographic appearance changed from dimple pattern to cleavage or quasi-cleavage pattern.
结果表明，随着峰值温度的提高，冲击韧性下降，断口形貌由韧窝状变成解理或准解理状。 - Their main cleavage pattern were thiadiazole broken, carbonyl cleavage and neutral losses.
其主要裂解方式为噻二唑环开裂，硫代羰基裂解及中性丢失。 - The fractures of the alloys change from dimple to cleavage fracture with river pattern.
合金的断口形貌由韧窝向河流花纹状的解理形貌转变。 - It was found that on the stress corrosion cracking surfaces of the two alloys there was a corrosion product layer which showed various different scanning electron fractographs, such as smooth flat feature resembling cleavage fracture, or "mud-crack pattern" and so on.
结果发现两种铝合金在氯化物水溶液中的应力腐蚀开裂断口复盖着&层腐蚀产物，这层腐蚀产物可以呈现不同的扫描电镜断口形貌，如类似解理的平滑形貌，龟裂泥巴状形貌等等。 - With sintering temperature raised and particle size decreased, the diameter of sintering neck is increased, mechanical properties are raised, the fracture of tantalum is cleavage fracture, section present river pattern and absorbed energy of plastic deformation is very low.
随着烧结温度的提高，钽粉粒度的减小，烧结颈直径增大，力学性能随之提高；金属钽的断裂主要是解理断裂，断面呈现出河流花样，塑性变形所吸收的能量很低。